Microbiologically Influenced Corrosion of Q235 Carbon Steel by Aerobic Thermoacidophilic Archaeon Me
The effect of thermoacidophilic archaeon Metallosphaera cuprina (M.cuprina) on the corrosion of Q235 carbon steel in its......
Corrosion inhibition of carbon steel in hydrochloric acid by cationic arylthiophenes as new eco-frie
This study describes the adsorption behavior of three arylthiophene derivatives namely:2-(4-amidino-3-fluorophenyl)-5-[4......
The effect of simulated acidified marine aerosols on the corrosion morphology of carbon steel was studied using an in si......
...
Wear resistances of CO2 corrosion product iflms formed on P110 carbon steel at different CO2 partial pressures were inve......
Synergic Mechanism of an Organic Corrosion Inhibitor for Preventing Carbon Steel Corrosion in Chlori
The inhibition effect of dimethylethanolamine (DMEA) and its composite with carboxylic acid was studied with the electro......
Influence of the C-S-H Amount on [Cl-]/[OH-]Ratio of Simulated Concrete SPS and the Corrosion Suscep
Two kinds of simulated concrete pore solutions (SPSs) were treated with different amounts of synthetic calcium silicate ......
The Effect of Microbes in Eutrophic Lakes on The Corrosion Behavior of Carbon Steel in Initial Stage
The eutrophication of lakes in China is more and more serious in recent years.Carbon steel as the common material of hyd......
为了提高海洋用钢的表面性能,采用激光熔覆技术在Q235钢板表面熔覆了QAl-7铝青铜合金,并对其组织以及熔合线处的铜渗透现象进行了......
The inhibition behavior of an imidazoline derivative as an organic corrosion inhibitor for carbon steel in desalted ......
在在 Qinghai 暴露的碳钢和捱过的钢上形成的锈腌湖空气因为 6 个月被 X 光检查衍射(XRD ) 描绘，红外线的传播光谱学(红外) ，扫描电......
On the localised corrosion of carbon steel induced by the in-situ local damage of porous corrosion p
The effect of in-situ local damage of uniform porous corrosion products on the localised corrosion of carbon steel is in......
Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon S
The formation and development of corrosion products on carbon steel surface during the initial stage of atmospheric corr......
用电化学方法和金属电子显微分析技术，对碳钢换热器Ｕ形管高温区腐蚀失效原因进行了分析，高温区管外壁表面发生较严重腐蚀是多种因素共......
利用固体力学性质的微观理论，对一些常见合金材料的线胀系数、杨氏模量随温度的变化规律从实验和理论上进行了分析计算，两者相符甚好......
设计了一种用于土壤体系的腐蚀测试，参比／研究电极为平面同心同材料结构的新型三电极体系。这一电极体系能很好克服自腐蚀电位漂移的......
探讨了用４５钢代替Ｃｒ１２ＭｏＶ钢制作塔轮的可行性，研究了４５钢稀土渗硼机理及渗层厚度，组织，硼化物形态对磨损强度和耐磨性的影响。......
针对燃油、易燃液体等介质对碳钢危化品运输车的腐蚀,导致的介质污染现象,通过罐体内部的防腐处理,消除腐蚀现象,从而取消腐蚀裕量......
通过对钢液凝固时其气泡和非金属夹杂的形成机理分析，以及中间包内钢水流动数学模型研究，发现中间包的结构与操作对 20＃连铸管坯质量......
通过室内腐蚀挂片及电化学测量试验，研究了Ｂ级碳素船体钢三种常见焊接接头的耐海水腐蚀性能，结果表明：在海水中，接头的焊缝区最易到腐蚀......